Resistor Paste RP Series (5mΩ ~200mΩ)
Our resistor paste RP series are low sheet resistor paste designed for heating elements on SUS430 stainless steel, and alumina ceramic substrate for making thick film circuit.
The resistivity ranges from 5mΩ/sq to 200mΩ/sq while TCR ranges from 600ppm/℃ to 1500ppm/℃. Intermediate resistivity may be obtained by lending the two members of a TCR group.
Benefits of the resistor paste include:
- High power density
- High precision
- Small drift of resistance after re-firing
Resistance
| Model | Sheet Resistivity (mΩ/sq)±10% | TCR(ppm/℃)±10% |
|---|---|---|
| RP00515 | 5 | 1500 |
| RP0115 | 10 | 1500 |
| RP0315 | 30 | 1500 |
| RP0515 | 50 | 1500 |
| RP1015 | 100 | 1500 |
| RP2015 | 200 | 1500 |
| RP1006 | 100 | 600 |
| RP2006 | 200 | 600 |
Technical Parameters
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 5 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 10 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 30 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 50 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 100 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 200 |
| TCR(ppm/℃)±10% | 1500 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 100 |
| TCR(ppm/℃)±10% | 600 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Viscosity (Pa.S)(Brookfield DV1, 10rpm, 25±1℃) | 120~150 |
| Fineness(μm) | ＜12 |
| Screen Mesh(Stainless steel/ Polyester Mesh) | 200~300 |
| Leveling Time | At room temperature, 3 min |
| Recommended Drying Conditions | 150℃/ ≥10min |
| Recommended Firing Conditions | 850℃/10min |
| Fired Thickness (μm) | 12~14 |
| Spreading Rate(cm2/g) (fired thickness:13μm) | ~100 |
| Sheet Resistivity (mΩ/sq)±10% | 200 |
| TCR(ppm/℃)±10% | 600 |
| Shelf Life | Six Months from Date of Shipment |