Medium Temperature Sintering Silver Paste for Glass Substrate CP600x
Our silver paste CP600x series is environmental conductive paste specially designed for automobile front windshield defogging. It is with firing temperature of 600℃ to 650℃.
It is non-toxic up to European RoHS environmental regulation.
Benefits of the silver paste include:
- Maximization of the range of temperature of sintering
- Strong adhesion, good weldability, excellent ageing resistance
- Small change of resistance with long-time printing
- Good compatibilities with black glaze
- Low technical sensitivity, highly acceptability
Typical Application:
- Automobile front windshield Defogging
Technical Parameters
| Test | Properties |
|---|---|
| Ag Content (%) | 80±2 |
| Viscosity (Pa.S)(Brookfield DV1,SC4-14,10rpm,25±0.5℃) | 30~35 |
| Fineness(μm) | ≤15 |
| Screen Mesh( Polyester Mesh) | 150~250 |
| Leveling Time | At room temperature, 2-3 min |
| Recommended Drying Conditions | 150℃~180℃/ 3~5min |
| Recommended Firing Conditions | 600-650℃/ 3min |
| Fired Thickness (μm) | 8~15 |
| Conductivity (mΩ/sq) | ≤ 3 |
| Drift of Resistance after Reliability Test (%) | ＜10 |
| Adhesion((N) | ≥130 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Ag Content (%) | 75±2 |
| Viscosity (Pa.S)(Brookfield DV1,SC4-14,10rpm,25±0.5℃) | 31~35 |
| Fineness(μm) | ≤15 |
| Screen Mesh( Polyester Mesh) | 150~250 |
| Leveling Time | At room temperature, 2-3 min |
| Recommended Drying Conditions | 150℃~180℃/ 3~5min |
| Recommended Firing Conditions | 600-650℃/ 3min |
| Fired Thickness (μm) | 8~15 |
| Conductivity (mΩ/sq) | ≤ 4 |
| Drift of Resistance after Reliability Test (%) | ＜10 |
| Adhesion((N) | ≥130 |
| Shelf Life | Six Months from Date of Shipment |
| Test | Properties |
|---|---|
| Ag Content (%) | 60±2 |
| Viscosity (Pa.S)(Brookfield DV1,SC4-14,10rpm,25±0.5℃) | 35~45 |
| Fineness(μm) | ≤15 |
| Screen Mesh( Polyester Mesh) | 150~250 |
| Leveling Time | At room temperature, 2-3 min |
| Recommended Drying Conditions | 150℃~180℃/ 3~5min |
| Recommended Firing Conditions | 600-650℃/ 3min |
| Fired Thickness (μm) | 8~15 |
| Conductivity (mΩ/sq) | ≤ 6~7.5 |
| Drift of Resistance after Reliability Test (%) | ＜10 |
| Adhesion((N) | ≥80 |
| Shelf Life | Six Months from Date of Shipment |